STUDI KUAT LENTUR PADA BETON TANPA AGREGAT KASAR DENGAN SERAT BAJA
Article Sidebar
Read Counter : 3
Download : 1
Main Article Content
Abstract
This research investigates the flexural strength of Reactive Powder Concrete (RPC) reinforced with micro steel fibers and designed without coarse aggregates. RPC is an advanced cementitious composite characterized by its dense matrix and ultra-high compressive strength, achieved through the use of ultra-fine materials such as quartz sand, silica fume, and marble powder. The addition of micro steel fibers is intended to enhance the flexural capacity and ductility of the concrete. A total of six beam specimens measuring 100 × 100 × 400 mm were tested using the third-point loading method in accordance with ASTM C78. All specimens underwent steam curing for 28 days. The results show that fiber-reinforced RPC significantly improves flexural performance, with values exceeding 300 MPa and compressive strengths averaging above 80 MPa. These findings suggest that fiber-reinforced RPC offers a promising alternative for high-performance structural applications and has strong potential for implementation in Indonesia due to the local availability of raw materials and compatible production methods.
Abstrak
Penelitian ini bertujuan untuk menganalisis kuat lentur beton Reactive Powder Concrete (RPC) yang diperkuat dengan serat baja dan tidak menggunakan agregat kasar. RPC merupakan jenis beton inovatif yang memiliki kepadatan tinggi dan kuat tekan sangat tinggi karena menggunakan material berukuran sangat halus seperti pasir kuarsa, silica fume, dan tepung marmer. Penambahan serat baja mikro dalam campuran RPC dilakukan untuk meningkatkan kekuatan lentur dan daktilitas beton. Pengujian dilakukan terhadap enam sampel balok berukuran 100 × 100 × 400 mm dengan metode third-point loading sesuai standar ASTM C78. Perawatan dilakukan selama 28 hari dengan metode uap panas. Hasil pengujian menunjukkan bahwa penggunaan serat baja dalam RPC mampu meningkatkan kekuatan lentur secara signifikan, mencapai nilai di atas 300 MPa, dengan kuat tekan rata-rata di atas 60 MPa. Temuan ini menunjukkan bahwa RPC berserat dapat menjadi alternatif beton struktural berkinerja tinggi yang layak dikembangkan di Indonesia karena ketersediaan bahan dan peralatan lokal yang mendukung.
Article Details
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
This work is licensed under Jurnal Mitra Teknik Sipil (JMTS) Creative Commons Attribution-ShareAlike 4.0 International License.References
ACI Committee 318. (2019). Building code requirements for structural concrete (ACI 318M-19).
ASTM. (2018) Standard test method for flexural strength of concrete (using simple beam with third-point loading) (ASTM C78/C78M-18). https://doi.org/10.1520/C0078_C0078M-21
Christianto, D., Pranoto, W. A., Jusuf, A. H., Kho, D. A., & Tavio (2024). Formulasi faktor modifikasi kuat tarik belah untuk kuat geser beton tanpa agregat kasar. Jurnal Mitra Teknik Sipil, 7(2), 663–670. https://doi.org/10.24912/jmts.v7i2.28994
Christianto, D., Utami, T. A., & Yoana, M. (2023). Sifat mekanik beton tanpa agregat kasar. Jurnal Mitra Teknik Sipil, 6(1), 145–158. https://doi.org/10.24912/jmts.v6i1.21637
Gea, P. M., Dohare, G. A., Zebua, M. K., Zebua, A. K., Zebua, D., & Ndruru, R. J. (2024). Pengaruh penambahan serat baja terhadap kuat tekan beton pada berbagai tingkat kepadatan. IDENTIK: Jurnal Ilmu Ekonomi, Pendidikan dan Teknik, 1(1), 66–73. https://doi.org/10.70134/identik.v1i1.246
Huseiny, M. S. A. & Nursani, R. (2020). Pengaruh bahan tambah serat fiber terhadap kuat tekan dan lentur beton. Akselerasi : Jurnal Ilmiah Teknik Sipil, 1(2), 63–69. https://doi.org/10.37058/aks.v1i2.1505
Kurniawan, S. (2016). Analisa perawatan beton cetak menggunakan uap. TAPAK (Teknologi Aplikasi Konstruksi): Jurnal Program Studi Teknik Sipil, 5(2), 98–107. https://doi.org/10.24912/jmts.v6i1.21637
Kushartomo, W., Christianto, D., & Suryani, J. (2016). Pengaruh penggunaan serat baja terhadap flexural toughness reactive powder concrete. Jurnal Teknik Sipil, 23(2), 107–112. https://doi.org/10.5614/jts.2016.23.2.3
Kushartomo, W. & Christianto, D. (2015). Pengaruh serat lokal terhadap kuat tekan dan kuat lentur reactive powder concrete dengan teknik perawatan penguapan. Jurnal Teknik Sipil, 22(1), 31–36. https://doi.org/10.5614/jts.2015.22.1.4
Linggasari, D., Sutandi, A., & Kushartomo, W. (2018). Pengaruh tepung marmer terhadap sifat mekanik reactive powder concrete. Jurnal Muara, Sains, Teknologi, Kedokteran, dan Ilmu Kesehatan, 2(2), 556–565. https://doi.org/10.24912/jmstkik.v2i2.3013
Mayhoub, O. A., Nasr, E. S. A., Ali, Y. A., & Kohail, M. (2021). The influence of ingredients on the properties of reactive powder concrete: A review. Ain Shams Engineering Journal, 12(1), 145–158.
Richard, P., & Cheyrezy, M. (1995). Composition of reactive powder concretes. Cement and concrete research, 25(7), 1501–1511.