CARA MUDAH MENENTUKAN MATERIAL TERBAIK DALAM STRUKTUR JALAN MENGGUNAKAN METODE MARSHALL TEST
Article Sidebar
Main Article Content
Abstract
Laston (concrete asphalt layer) consists of continuous aggregate grades of various grain sizes and asphalt mixtures. Different aggregate sizes produce asphalt mixtures with high stability. But in reality on the ground is still not fully in accordance with what was expected. Therefore, in this study, further investigations were carried out related to the material that makes up the road pavement layer, especially the use of materials originating from the Brantas River in the Kediri area, while the tests carried out were in the form of aggregate characteristics tests and marshall tests. From each test above, 3 test samples were used to validate the values obtained. The reference method is SNI and SU-2018. From the results of the study, it is known that the use of material from the Brantas River has good physical properties and durability, this is shown from the material characteristics test value that meets the SU-2018, the characteristic value has an impact with a good stability value. So that the use of material from the Brantas River is able to provide an alternative as one of the materials in the road pavement layer structure.
Abstrak
Laston (lapisan aspal beton) terdiri dari nilai agregat kontinu dari berbagai ukuran butir dan campuran aspal. Ukuran agregat yang berbeda-beda menghasilkan campuran aspal dengan stabilitas tinggi. Namun pada kenyataan dilapangan masih belum sepenuhnya sesuai dengan apa yang diharapkan. Oleh karena itu pada penelitian ini dilakukan penyelidikan lebih lanjut terkait material penyusun lapis perkerasan jalan khususnya penggunaan material yang berasal dari sungai brantas area kediri, sedangkan uji yang dilakukan berupa uji karakteristik agregat dan uji marshall. Dari setiap uji diatas digunakan 3 sample uji untuk memvalidasi nilai yang didapatkan. Metode acuan yakni SNI dan SU-2018. Dari hasil penelitian diketahui bahwa penggunaan material dari sungai brantas memiliki sifat fisik dan juga daya tahan yang bagus, ini ditunjukkan dari nilai uji karakteristik material memenuhi SU-2018, nilai karakteristik itu berdampak dengan nilai stabilitas yang baik. Sehingga penggunaan material dari sungai brantas ini mampu memberikan alternatif sebagai salah satu material dalam struktur lapis perkerasan jalan.
Article Details
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.
This work is licensed under Jurnal Mitra Teknik Sipil (JMTS) Creative Commons Attribution-ShareAlike 4.0 International License.References
Ambarura, D. J. M., Alpius, & Elizabeth. (2021). Karakteristik Campuran AC-BC Menggunakan Batu Sungai Salo Pattejang Kecamatan Bungoro Kabupaten Pangkep. Paulus Civil Engineering Journal, 3(4), 570–576. https://doi.org/10.52722/pcej.v3i4.336
Badan Standardisasi Nasional. (1990). Metode Pengujian Tentang Analisis Saringan Agregat Halus dan Kasar (SNI 03-1968-1990)
Badan Standardisasi Nasional. (1991). Metode Pengujian Campuran Aspal dengan Alat Marshall (SNI 06-2489-1991).
Badan Standardisasi Nasional. (2004). Geometri Jalan Perkotaan (RSNI T-14-2004).
Badan Standardisasi Nasional. (2008). Cara Uji Keausan Agregat dengan Mesin Abrasi Los Angeles (SNI 2417:2008).
Choudhary, J., Kumar, B., & Gupta, A. (2020). Utilization of Solid Waste Materials as Alternative Fillers in Asphalt Mixes: A Review. Construction and Building Materials, 234, 117271. https://doi.org/10.1016/j.conbuildmat.2019.117271
Direktorat Jenderal Bina Marga. (2018). Spesifikasi Umum 2018 untuk Pekerjaan Konstruksi Jalan dan Jembatan (SU-2018). Lampiran Dirjen Bina Marga Nomor 02/SE/Db/2018.
Guo, Q., Wang, H., Gao, Y., Jiao, Y., Liu, F., & Dong, Z. (2020). Investigation of the low-temperature properties and cracking resistance of fiber-reinforced asphalt concrete using the DIC technique. Engineering Fracture Mechanics, 229, 106951. https://doi.org/10.1016/j.engfracmech.2020.106951
Hassan, H. M. Z., Wu, K., Huang, W., Chen, S., Zhang, Q., Xie, J., & Cai, X. (2021). Study on the influence of aggregate strength and shape on the performance of asphalt mixture. Construction and Building Materials, 294, 123599. https://doi.org/10.1016/j.conbuildmat.2021.123599
Kim, M. J., Kim, S., Yoo, D. Y., & Shin, H. O. (2018). Enhancing mechanical properties of asphalt concrete using synthetic fibers. Construction and Building Materials, 178, 233–243. https://doi.org/10.1016/j.conbuildmat.2018.05.070
Liu, P., Xu, H., Wang, D., Wang, C., Schulze, C., & Oeser, M. (2018). Comparison of mechanical responses of asphalt mixtures manufactured by different compaction methods. Construction and Building Materials, 162, 765–780. https://doi.org/10.1016/j.conbuildmat.2017.12.082
Movilla-Quesada, D., Raposeiras, A. C., Silva-Klein, L. T., Lastra-González, P., & Castro-Fresno, D. (2019). Use of Plastic Scrap in Asphalt Mixtures Added by Dry Method as a Partial Substitute for Bitumen. Waste Management, 87, 751–760. https://doi.org/10.1016/j.wasman.2019.03.018
Nugroho, M. S. (2019). Karakteristik Marshall Quotient Pada Hot Mix Asphalt Menggunakan Agregat Alam Sungai Opak. INERSIA: Informasi dan Ekspose Hasil Riset Teknik Sipil dan Arsitektur, 15(2), 84–91. https://doi.org/10.21831/inersia.v15i2.28627
Putra, K. H., & Wahdana, J. (2019). Studi Eksperimental Penambahan Limbah Keramik Sebagai Agregat Halus pada Campuran Laston (AC-WC) terhadap Karakteristik Uji Marshall. Paduraksa: Jurnal Teknik Sipil Universitas Warmadewa, 8(2), 147-155. https://doi.org/10.22225/pd.8.2.1396.147-155
Safariadi, Erwan, H. K., & Akhmadali. (2018). Karakteristik Campuran Beraspal (Laston) Akibat Pengaruh Penggunaan Instant Powder Sebagai Pengganti Filler. JeLAST: Jurnal PWK, Laut, Sipil, Tambang, 5(1), 1-15. http://dx.doi.org/10.26418/jelast.v5i1.24203
Salmon, N. A., Alpius, & Kamba, C. (2020). Pemanfaatan Batu Gunung Posi’padang Balla Kabupaten Mamasa Sebagai Campuran AC-BC. Paulus Civil Engineering Journal, 2(2), 77-84. https://doi.org/10.52722/pcej.v2i2.134
Simanjuntak, A. J., Desriantomy, & Silitonga, S. P. (2021). Pemanfaatan Abu Serbuk Kayu Sebagai Tambahan Filler pada Campuran Perkerasan Jalan Jenis HRS-WC (Hot Rolled Sheet-Wearing Course). Jurnal Teknika: Jurnal Teoritis dan Terapan Bidang Keteknikan, 5(1), 1-10. https://doi.org/10.52868/jt.v5i1.4525
Syaviq, M. F., Arifin, M. Z., Bowoputro, H., Djakfar, L., & Ambarwati, L. (2018). Studi Pengaruh Penambahan Serabut Kelapa Terhadap Karakteristik Marshall Pada Campuran Aspal Porus. Rekayasa Sipil, 12(2), 92-98. https://doi.org/10.21776/ub.rekayasasipil.2018.012.02.3
Syaripin, Suparma, L. B., & Mulyono, A. T. (2021). Pengaruh Substitusi Limbah Kaca terhadap Agregat Halus Pada Campuran Laston AC-BC. Prosiding Forum Studi Transportasi antar Perguruan Tinggi, Indonesia, 24, 472. https://ojs.fstpt.info/index.php/ProsFSTPT/article/view/806